YKBD- (J/S) series of two component low temperature baking paint


The main products in order to meet the high temperature baking conditions do not have to use the flood, the products can also be their own drying, widely used in lighting glass, flat glass, wash, sanitary ware and courage courage handicraft decoration.

YKBG-J000 series of metallic glass paint

Characteristic:

This product can make the color changing glass paint from multi angle, give a person with a magic effect.

Technical indicators:

Appearance: gray brown viscous liquid.

Hardness: H-2H (the pencil)

Resistance of 75% alcohol: 3 hours do not fade, do not fall off.

Adhesion: 1*1mm grid cut, tape, no shedding.

Construction proportion:

YKBG-J000 series: curing agent YK-200: YKQT-017=100:30:0.8 (50-70).

The curing conditions:

Since the dry at room temperature, can be 60 to 80 DEG C for 40 minutes, 24 hours after thetest performance.

Note:

1, to ensure that no impurities and oil the surface of glass objects, after spray on the ventilation dust at 5-10 minutes, gradually heating.

Adding 2, YKQT-017 assistant: first the additive mixing a little dilution, then added to the mix of glass paint use thinner coating viscosity, good paint recommended within 4 hours of use.

The above information we obtained, experiments under special conditions are for reference only, the actual operating conditions of your own test.

Packaging: 4 kg / barrel, 20 kg / barrel, 180 kg / barrel.

YKBG-S000 series of metallic glass paint

Characteristic:

This product is rich in color, high hiding power, excellent adhesion on the surface of glass.

Technical indicators:

Appearance: gray brown viscous liquid.

Hardness: HB-H (the pencil)

Resistance of 75% alcohol: 3 hours do not fade, do not fall off.

Adhesion: 1*1mm grid cut, tape, no shedding.

Construction proportion:

YKBG-S000 series: YK-200: YKQT-017: curing agent, diluent diluent YK-101=100:50: (40-60)

The curing conditions:

Since the dry at room temperature, can be 60 to 80 DEG C for 40 minutes, 24 hours after thetest performance.

Note:

1, to ensure that no impurities and oil the surface of glass objects, after spray on the ventilation dust at 5-10 minutes, gradually heating.

Adding 2, YKQT-017 assistant: first the additive mixing a little dilution, then added to the mix of glass paint use thinner coating viscosity, good paint recommended within 4 hours of use.

The above information we obtained, experiments under special conditions are for reference only, the actual operating conditions of your own test.

Packaging: 4 kg / barrel, 20 kg / barrel, 180 kg / barrel.


清远雅克化工有限公司 @ All rights reserved 2015 | 粤ICP备06084242号 | The website construction:Qingyuan rubik's cube network
address:Qingyuan city, guangdong province high-tech development zone Silver light jia fu jia by 16 industrial zone tel:0763-3607328 email:yakoo@yakoo.com.cn

在线客服

树脂
点击这里给我发消息
原子灰
点击这里给我发消息
工业漆
点击这里给我发消息
点击这里给我发消息