Wide range of application, high cost performance.Easy grinding, good adhesion, and post curing fast, suitable for fast repairing fast repair.Widely used for cars, trucks, machine tools, machinery, ships, furniture, and on the building is decorated also have application.
Steel, iron, glass, wood, concrete, old paint layer, etc
Ratio of the construction
Atomic ash: curing agent = 100:1.5 3 (weight ratio)
Note: the operational time 5 to 7 minutes (according to the proportion of curing agent and temperature changes in different)
The construction technology
Substrate processing: use P80 - P120 for blowing ash substrate surface of sand paper burnish, go to the oil and water, dry.
Mixed aside: will the Lord grey and curing agent 100:1.5 3 mixed evenly, make the colour and lustre is consistent.
Blade coating that will mix good atomic ash in 5-7 minutes / 25 ℃ operational time, coating on the treated surface of the substrate.
40 to 60 minutes after polishing, coating / 25 ℃, can be polished.
Matters needing attention
1. The surface if there are air bubbles infiltration, must be thoroughly with scraper, leveling in order to ensure good adhesion.
2. If need thick coating, several times the best thin blow to the required thickness.
3. Has not used up of putty and hardener should be kept sealed, atomic ash with curing agent added back into the tank.
4. Store in a cool, dry place, away from heat and fire, avoid direct sunlight.
5. Shelf life: 6 months / 25 ℃.